Byk Epoxy Tc 9202-2K
Solvent Free Epoxy Top Coat
BYK EPOXY TC 9202–2K two component, solvent free, easy to apply and smooth surface finish , non- slip epoxy final top coating material designed for industrial floors.
Places of Usage
• Factories, warehouses, shopping malls, aircraft hangars,
• Schools, hospitals, pharmaceutical industry, food industry, laboratories, parking lots,
• Wastewater treatment plants, areas where heavy forklifts and corrosive chemicals are used
Avantajları
• Solvent free,
• High mechanical strenght,
• High liquid permeability.
• Glossy finish coat
• Easy to apply
• Easy to clean and maintanance.
• Non slip surface.
Technical Specifications
Renk |
A Comp. : Ral Colors B Comp.: Transparent |
- | |
Yoğunluk |
A Comp:1,70±0,1 g/cm3 B Comp: 1,0 ±0,1 g/cm3 |
- | |
Hardness (7 days |
>75 Shore D | ASTM D1475 / DIN 53217 / ISO 2811, @ 20oC | |
Viskcosity (Mixture) |
1500 cP | ASTM D2240 / DIN 53505 / ISO R868 | |
Mixing Ratio (A+B) |
19+5 By weight | ASTM D 2196-86 / EN ISO 3219 (+25°C) | |
Abrasion Strenght (7 days) |
30-35 mg | - | |
Compressive Strenght |
50 (N/mm2) | - | |
Eğilme Mukavemeti 28 gün |
20 (N/mm2) | EN 196-1 | - |
Adhesion to Concrete |
1,5 (N/mm2) | - | - |
Kullanma Süresi |
40-60 min | ASTM D4541 | - |
NOTE: Flammable and exploision products should be kept away during the application. Protective gloves and masks should be used for hands and eyes during application. The product should be used in well ventilated environments.If the material comes into contact with eyes, it should be washed immediately with su¬cient water. Childrens should kept away from the product. For more detailed information, ask for the Safety Data Sheet (MSDS).
Karıştırma
Component A and Component B are supplied in separate packages in predetermined mixing ratios. Component B must be completely emptied into Component A and mixed thoroughly. Mixing should be carried out using a mechanical mixer at 300 rpm. As this is a two-component product, only the amount to be used should be prepared in accordance with the specified mixing ratio, taking the pot life into consideration. To obtain a homogeneous mixture, ensure that the product temperature is not below 15°C. Component A should first be pre-mixed briefly using a mechanical mixer. Then, the hardener (Component B) should be added in the correct mixing ratio. Components A and B must be mixed with a mechanical mixer for at least 3 minutes until a homogeneous mixture is achieved. The prepared mixture should be used within its specified pot life.
Uygulama
The mixture prepared for application should be applied in two directions using a short-nap roller. During application, the relative humidity of the air must not exceed 80%, and the application temperature (ambient and substrate) must be between +10°C and +30°C. For outdoor applications, there must be no rainfall 24 hours before application, during application, and for 24 hours after application. The substrate temperature must be at least 3°C above the current dew point temperature. Applied surfaces must be protected for at least 24 hours. The material reaches the mechanical properties specified in the Technical Data Sheet approximately 7 days after application.
Surface Preparation
For Metal Surfaces: In order to achieve top level performance, sandblasting should be done at Sa 2 ½ level.The sandblasted surface should be primed with a dust rich epoxy primer or phosphate rich epoxy primer to form the required dry film before recording product identification information.
For Concrete Surfaces: The concrete surface must be clean, solid and have sufficient compressive strength (>25N/mm2), and tensile strength must be >1.5N/mm2. The concrete floor to be insulated must be solid and there must be no movement on the surface. The grout layer on the surface must be removed. The concrete to be insulated must be at least C25 and preferably C30 – C35 standard.
Concrete Standards: The surface should be cleaned with pressurized water and freed from oil, grease, dirt, mortar particles and dust. Concrete surfaces should be prepared to obtain an open porous surface by removing cement grout using abrasive equipment.It should also be completely cleaned from mold release agents, cement residues, shavings, loose particles and uncured membranes. The grout layer on the surface must be removed. (Shot-Blast, Rota Tiger etc.) If the surface is too shiny, it should be roughened with milling or sandblasting. Concrete cracks should be cut in a V shape, cleaned and false joints should be cleaned.
• Hardness :R28 = 15 Mpa
• Temperature 10-30°C
• Humidity: < 4%
Packaging
A + B comp. part: 19 +5 kg in metal buckets
Sarfiyat
Minimum total consumption: 0,7-0,9 kg/m2
Raf Ömrü
Güvenlik Önlemleri
Responsibility
Yapıştırıcı Grubu çimento esaslı, kayma özelliği azaltılmış, iç ve dış mekânlarda, yatay ve düşeyde kullanılabilen seramik yapıştırma malzemesidir.